There are provided a rare-earth permanent magnet based on Nd-Fe-B, capable of improving coercive force through reducing a residual nitrogen concentration after sintering to be 800 ppm or lower, and a manufacturing method of the rare-earth permanent magnet. The rare-earth permanent magnet based on Nd-Fe-B is obtained through milling a magnet material in an atmosphere of a noble gas by dry milling, and thereafter, compacting the milled magnet material into a formed body in an atmosphere of a noble gas. The formed body is then sintered at 800 through 1180 degrees Celsius so as to obtain a permanent magnet 1 whose nitrogen concentration is 800 ppm or lower, or more preferably 300 ppm or lower. |