The present invention relates to a fabricating method for an Mn-Al based powder which comprises the steps of : fabricating the Mn-Al based powder; fabricating a pre-treatment solution; fabricating an electroless plating solution; removing an oxide film of the Mn-Al based powder by mixing the Mn-Al based powder and a pre-treatment solution; fabricating the Mn-Al based powder solution which contains a portion of the pre-treatment solution wherein part of the pre-treatment solution is volatilized; and forming a metal shell on the Mn-Al based powder core by inserting the Mn-Al based powder into the electroless plating solution. As a magnetic material, the Mn-Al based powder which receives attention has a particle structure as a core-shell structure, thereby realizing a hard and soft magnetism composite structure to replace a conventional rare-earth based magnet by developing a high efficiency magnetic material through exchange-coupling.(BB) End(AA) Start(S120) Step of removing an oxide film of the Mn-Al based powder by mixing the Mn-Al based powder and the pre-treatment solution(S130) Step of fabricating Mn-Al based powder solution including a partial pre-treatment solution by volatilizing part of the pre-treatment solution(S140) Step of forming a metal shell on Mn-Al based powder core by inserting Mn-Al based powder solution(S111) Step of fabricating an Mn-Al based powder(S112) Step of fabricating a pre-treatment solution including hypophosphorous acid based material(S113) Step of fabricating a plating solutionCOPYRIGHT KIPO 2015 |
客服热线：
手机版
二维码