The composition of the invention is based on oxides of cerium, of zirconium and of at least one rare earth metal other than cerium, with a cerium oxide content of greater than 50% by weight and it has, after calcination at 1000°C for 4 hours, a specific surface area of at least 20 m2/g and an amount of mobile oxygen between 200°C and 400°C of at least 0.8 ml O2/g. It is prepared by a process in which, in a reactor, a mixture of compounds of cerium, of zirconium and of the other rare earth metal is reacted continuously with a basic compound with a residence time of the reaction medium in the mixing zone of the reactor of at most 100 milliseconds; the precipitate is heated then brought into contact with a surfactant before being calcined. |