The present invention relates to a glazing paste composition for dental porcelain and a method for manufacturing the same and, more specifically, a glazing paste composition for dental porcelain with excellent durability and glossiness and a method for manufacturing the same. The glazing paste composition for dental porcelain of the present invention is formed by mixing 40-60 parts by weight of additive liquid with respect to 100 parts by weight of frit powder. The frit powder is formed by grounding hyalin obtained by melting a porcelain mixture of 60-70 wt% of silica (SiO_2), 10-15 wt% of alumina (Al_2O_3), 10-15 wt% of sodium oxide (Na_2O), 3-6 wt% of potassium oxide (K_2O), 3-5 wt% of calcium oxide (CaO), and 2-6 wt% of boron oxide (B_2O_3).COPYRIGHT KIPO 2019 |