The disclosure provides a rare earth anisotropic hard magnetic material, which has, on atomic percent basis, a composition of (Sm1-αRα)xFe100-x-y-zMyIz, wherein, R is Pr alone or a combination of Pr with at least one rare earth element selected from the group consisting of La, Ce, Nd, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu and Y; M is at least one element selected from the group consisting of Si, Ti, V, Cr, Mn, Co, Ni, Cu, Zn, Nb, Mo, Al, and Zr; I is N alone or a combination of N and C; 0.01≦α≦0.30; 7≦x≦12, 0.01≦y≦8.0, 6≦z≦14.4, and which anisotropic rare earth hard magnetic material is crystallized in a Th2Zn17-type structure, of which crystalline grains are in a flake shape with a gain size ranging from 1 to 5 μm, and c-axis of the crystalline grains, an easy magnetization direction, being oriented along the minor axis of the flake crystalline grains. The disclosure also provides a process for producing the powdery rare earth anisotropic hard magnetic material and a process for producing anisotropic calender flexible magnet. |