Formation of intermetallic phases such as sigma (Ã) and khi (Ç) shows detrimental effects on the corrosion and mechanical properties of high-grade duplex stainless steel. The present invention provides high-grade duplex stainless steel with much suppressed formation of intermetallic phases, of which the chemical composition consists essentially, on a weight basis, of : Cr : 21.0% - 38.0%, Ni : 3.o% - 12.0%, Mo : 1.5% - 6.5%, W : 6.5% or less, Si : 3.0% or less, Mn : 8.0% or less, N : 0.2% - 0.7%, C : 0. 1% or less, at least one element selected from the group consisting of Ba : 0.0001 - 0.6% and one or more elements of Mischmetal (MM) and Y : 0.0001 - 1.0% in total, and a balance of Fe and incidental impurities. The pitting resistance equivalent has a value of 40 ‰ PREW ‰ 67 defined by the following formula (1) : PREW = wt.%Cr + 3.3(wt.%Mo + 0.5wt.%W) + 30wt.% N-----(1) The present high-grade duplex stainless steel exhibits an excellent corrosion resistance, embrittlement resistance, castability and hot workability. |