The invention relates to a precursor compound of an alkaline earth metal or a rare earth metal aluminate of formula : a(M1O).b(MgO).c(AI2O3) or a(M 2O1.5).b(MgO).c(AI2O3), where M1 = an alkaline earth metal and M2 = yttrium or a combination of cerium and terbium and a, b et c are either whole numbers or not and obey the relationships : 0.25 = a = 4; 0 = b = 2 et 0.5 = c = 9, crystallized in the form of a transition alumina comprising essentially spherical and chemically homogeneous particles. Said particles have pores the average diameter of which is less than 10 nm. The above is obtained by a method in which a liquid mixture is formed comprising compounds of aluminium and other elements present in the composition of the precursor, said mixture is dried by atomisation and the dried product calcinated at a temperature between 700°C and 950°C inclusive. An alkaline earth metal or a rare earth metal aluminate is obtained by subsequent calcination of the product obtained.