Low-temperature sintered barium titanate microwave dielectric ceramic material

文件类型：PDF文档
文件大小：840K
The present invention relates to a low-temperature sintered barium titanate microwave dielectric ceramic material. The host matrix thereof can be represented by BaxTiyMzOx+2y+k, where x is 1˜6, y is 1˜17, z is 0˜1, k is 0˜3, M is an element substituting the Ba or Ti ion, for example selected from an alkali metal, an alkaline-earth metal, a transition group or a rare earth group, and preferably Ba2Ti9O20 or the host matrix containing Zr, Sn, Zn, etc. According to the present invention, a low melting glass is added and a subsequent milling operation is performed to reduce the sintering temperature of the microwave dielectric ceramic material to less than 1, 000° C. The low melting glass can be for example the Ba—B—Si—Li glass, Ba—B—Zn—Si—Li glass, Ba—B—Si—Li—Cu glass or Cu—B—Zn—Si—Li glass.